ISO 7441:2015 PDF

Corrosion of metals and alloys — Determination of bimetallic corrosion in atmospheric exposure corrosion tests

Открыть превью (PDF)

Название (английский):

ISO 7441:2015

Corrosion of metals and alloys — Determination of bimetallic corrosion in atmospheric exposure corrosion tests

Статус документа:: Действующий
Формат:: Электронный (PDF)
Количество страниц:: 14
Дата публикации:: 5 января 2015 г.
Издание:: ISO IS 7441 edition 2 version 1
ICS:: 77.060

Язык документа:

ruen

Срок поставки:3 раб. дн. (перевод)

Цена:210 €

Описание (английский):

ISO 7441:2015 specifies and compares methods for the determination of bimetallic corrosion of metals and coated metals in atmospheric exposure corrosion tests. The methods are intended for the determination of the amount and type of corrosion effect, arising in natural atmospheres, caused by contact with different metals.

Технические детали

Технический комитет: ISO/TC 156 - Corrosion of metals and alloys
SKU: ISO 7441:2015

Abstract

Overview

ISO 7441:2015 - "Corrosion of metals and alloys - Determination of bimetallic corrosion in atmospheric exposure corrosion tests" - specifies and compares standardized methods to determine bimetallic (galvanic) corrosion of metals and coated metals under natural atmospheric exposure. The standard describes how to prepare specimens, expose them, evaluate corrosion (amount and type), and calculate the bimetallic effect - the relative increase in corrosion caused by electrical contact between dissimilar metals in an atmosphere.

Key features:

Compares three test configurations: rectangular plates, washers, and wire-on-bolt.
Covers specimen types (test, reference, standard, control), preparation, exposure and evaluation procedures.
Intended to quantify bimetallic effects that typically act within about 0.5 cm of the contact point in atmospheric conditions.

Key technical topics and requirements

Test methods compared
- Rectangular plates - allows evaluation of mechanical properties in addition to mass loss; recommended for tensile testing specimens (thickness 1–6 mm).
- Washers - useful when the anodic material is not known in advance.
- Wire-on-bolt - shorter exposure time (typically >90 days acceptable) but consult ASTM G116 for full method details.
Specimen preparation
- Types: test, reference, standard, control.
- Surface condition: free of visible defects; surface roughness better than 2.5 µm (0.4–0.5 µm recommended).
- Coated metals must follow appropriate coating standards (e.g., ISO 1456, ISO 2081, ISO 7599).
Assembly and electrical checks
- Use insulating washers/sleeves (ceramics, polyethylene/polypropylene) to isolate bolts.
- Bolts/washers typically stainless steel grade 1.4301/304 or higher.
- Typical tightening torque ≈ 1.0 ± 0.1 N·m; verify insulation (>10 kΩ between bolt and washers) and contact resistance (

Overview

Key features:

Compares three test configurations: rectangular plates, washers, and wire-on-bolt.
Covers specimen types (test, reference, standard, control), preparation, exposure and evaluation procedures.
Intended to quantify bimetallic effects that typically act within about 0.5 cm of the contact point in atmospheric conditions.

Key technical topics and requirements

Test methods compared
- Rectangular plates - allows evaluation of mechanical properties in addition to mass loss; recommended for tensile testing specimens (thickness 1–6 mm).
- Washers - useful when the anodic material is not known in advance.
- Wire-on-bolt - shorter exposure time (typically >90 days acceptable) but consult ASTM G116 for full method details.
Specimen preparation
- Types: test, reference, standard, control.
- Surface condition: free of visible defects; surface roughness better than 2.5 µm (0.4–0.5 µm recommended).
- Coated metals must follow appropriate coating standards (e.g., ISO 1456, ISO 2081, ISO 7599).
Assembly and electrical checks
- Use insulating washers/sleeves (ceramics, polyethylene/polypropylene) to isolate bolts.
- Bolts/washers typically stainless steel grade 1.4301/304 or higher.
- Typical tightening torque ≈ 1.0 ± 0.1 N·m; verify insulation (>10 kΩ between bolt and washers) and contact resistance (

ISO 7441:2015 PDF

Технические детали

Abstract

Overview

Key technical topics and requirements

Похожие стандарты

Abstract

Overview

Key technical topics and requirements

Похожие стандарты

Metallic and other inorganic coatings. Electrodeposited coatings of nickel, nickel plus chromium, copper plus…

Metallic and other inorganic coatings — Electroplated coatings on iron and steel using zinc treated with solu…

Anodizing of aluminium and its alloys — Method for specifying decorative and protective anodic oxidation coat…